It is better welding Nylon using this welding method
This kind of welding way of robustness is better
It is better use this way to welding PC.
The leakage is better by this way
Welding line at about 1 mm
Two chamfer is 0.3
The interval from 0.08~0.12mm is the best
Slot of the wall thickness of 2.5 mm, both side 0.7 mm, welding slot to 1 mm, chamfering and redundant Angle of 0.3 * 0.3 minimum value for ultrasonic welding, can be raised according to different situations.
Nylon hygroscopicity can affect the ultrasonic wave and the fiber content more than 30% will also affect the ultrasonic welding
Terraced should be same for both side, but if different,the inner wall thickness little thinner than the outer wall , so will toward the direction of the lining of the arch welding, and will not affect the appearance,